High Quality Welding Electrodes Aws E6011
China High Quality Welding Electrodes Aws E6011, Find details about China Vertical Down Welding Electrode E6011, Welding Rods E6011 from High Quality Welding Electrodes Aws E6011 - Zibo Qilu Welding Industry Co., Ltd.
Description
Basic Info
- Model NO.: AWS E6011/DIN E4343C4/JIS D4311
- Material: Mild Steel
- Diameter:2.0mm/2.5mm/3.2mm/4.0mm/5.0mm: Length:300mm/350mm/400mm/450mm
- Specification: 2.5x300mm; 3.2x350mm; 4.0x400mm,
- HS Code: 83111000
- Type: E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
- Function: Low Hydrogen Type Electrode, High Efficient Iron Powder Electrode, Gravity Electrode
- Trademark: QILU BRAND
- Origin: Shangdong
Product Description
AWS E6011 is a kind of carbon steel electrode with cellulose potassium type coating specially used for vertical downward welding. AC/DC. It has excellent welding performance, beautiful appearance after vertical downward welding, fewer slags and high welding efficiency.
Applications:Suitable for butt welding, fillet welding and lap welding on thin plates, such as low-carbon steel structures like flues of power stations, air ducts, transformer oil tanks, hulls, exterior panels of cars, etc.
Applications:Suitable for butt welding, fillet welding and lap welding on thin plates, such as low-carbon steel structures like flues of power stations, air ducts, transformer oil tanks, hulls, exterior panels of cars, etc.
X-ray Radiographic Inspection: IIDegree
Instructions:
1. If the electrodes are affected with damp, they must be baked under 80ºC for 1.5 hours before welding.
2. The stains on the weldments, such as oil stains, rust, moisture etc., must be cleared away before welding.
3.The electrode weaving should not be too wide and the strength of the arc should be suitable.
Instructions:
1. If the electrodes are affected with damp, they must be baked under 80ºC for 1.5 hours before welding.
2. The stains on the weldments, such as oil stains, rust, moisture etc., must be cleared away before welding.
3.The electrode weaving should not be too wide and the strength of the arc should be suitable.
| Chemical Composition of Deposited Metal (%) | |||||
| Chemical Composition | C | Mn | Si | S | P |
| Guarantee Value | ≤0.20 | 0.30~0.60 | ≤0.30 | ≤0.035 | ≤0.040 |
| General Result | 0.097 | 0.58 | 0.21 | 0.017 | 0.018 |
| Mechanical Properties of Deposited Metal | |||||
| Test Item | Rm(MPa) | ReL(Mpa) | A(%) | AKV(J) | |
| Guarantee Value | ≥420 | ≥330 | ≥22 | ≥27(-30ºC) | |
| General Result | 508 | 406 | 28 | 75 | |
| Reference Current (AC, DC+) | |||||
| Diameter(mm) | φ2.0 | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
| Welding Current (A) | 30~50 | 70~100 | 90~140 | ||